TECATRON®PVX PPS modified CARBON FIBRES PTFE GRAPHITE

Get Latest Price

Min. Order:: 1 Kilogram

Min. Order:: 1 Kilogram

Transportation:: Ocean, Land, Air, Express

Port:: Shenzhen, Guangzhou, Hongkong

Quantity:

Your message must be between 20 to 2000 characters

Contact Now

Basic Info

Supply Ability:	100000
Payment Type:	T/T,Paypal
Incoterm:	FOB,CFR,CIF,EXW,DDU
Transportation:	Ocean,Land,Air,Express
Port:	Shenzhen,Guangzhou,Hongkong

Product Description

Through TECATRON PVX black, Ensinger offers a filled PPS (PPS CS CF TF), which is a specially modified for use in sliding applications. The material contains 10 % each of PTFE, graphite and carbon fibres which are added to the PPS to facilitate bearing and wear applications. The additives of the PPS compound result in an optimum coefficient of friction value, that makes the material ideally suited to dry running conditions. So TECATRON PVX is a bearing grade PPS that is suitable for high load applications, under high temperatures, and the effects of chemicals and steam. The PPS compound perfectly combines good mechanical properties with excellent thermal and chemical resistance properties.

Tecatron Pvx Black Jpg

FACTS

Chemical designation

PPS (Polyphenylensulfide)

Colour

black

Density

1.5 g/cm3

MAIN FEATURES

good heat deflection temperature

very good slide and wear properties

very good chemical resistance

inherent flame retardant

high stiffness

high dimensional stability

high creep resistance

TARGET INDUSTRIES

mechanical engineering

vacuum technology

oil and gas industry

aircraft and aerospace technology

automotive industry

Applications

Bushings & Bearings

Pump & Valve Parts

Thrust Washers

Mechanical properties

MECHANICAL PROPERTIES	VALUE	UNIT	PARAMETER	NORM
Modulus of elasticity (tensile test)	4600	MPa	1mm/min	DIN EN ISO 527-2
Tensile strength	53	MPa	50mm/min	DIN EN ISO 527-2
Tensile strength at yield	53	MPa	50mm/min	DIN EN ISO 527-2
Elongation at yield (tensile test)	2	%	50mm/min	DIN EN ISO 527-2
Elongation at break (tensile test)	2	%	50mm/min	DIN EN ISO 527-2
Flexural strength	91	MPa	2mm/min, 10 N	DIN EN ISO 178
Modulus of elasticity (flexural test)	4800	MPa	2mm/min, 10 N	DIN EN ISO 178
Compression modulus	3300	MPa	5mm/min, 10 N	EN ISO 604
Impact strength (Charpy)	14	kJ/m2	max. 7,5J	DIN EN ISO 179-1eU
Ball indentation hardness	238	MPa		ISO 2039-1
Compression strength	19/36/89	MPa	1% / 2% / 5%	EN ISO 604

Thermal properties

THERMAL PROPERTIES	VALUE	UNIT	PARAMETER	NORM
Glass transition temperature	94	C		DIN EN ISO 11357
Melting temperature	281	C		DIN EN ISO 11357
Thermal conductivity	0.58	W/(k*m)		ISO 22007-4:2008
Specific heat	0.9	J/(g*K)		ISO 22007-4:2008
Service temperature	260	C	short term	NN
Service temperature	230	C	long term	NN
Thermal expansion (CLTE)	5	10-5*1/K	23-60°C, long.	DIN EN ISO 11359-1;2
Thermal expansion (CLTE)	6	10-5*1/K	23-100°C, long.	DIN EN ISO 11359-1;2
Thermal expansion (CLTE)	13	10-5*1/K	100-150°C, long.	DIN EN ISO 11359-1;2

Electrical properties

ELECTRICAL PROPERTIES	VALUE	UNIT	PARAMETER	NORM
surface resistivity	104 -1010	Ω		DIN EN 61340-2-3
volume resistivity	107-1012	Ω*cm		DIN EN 61340-2-3

Other properties

OTHER PROPERTIES	VALUE	UNIT	PARAMETER	NORM
Resistance to hot water/ bases	+	-		-
Flammability (UL94)	V0	-	corresponding to	DIN IEC 60695-11-10;
Resistance to weathering	(+)	-		-
Water absorption	<0.01	%	24h / 96h (23°C)	DIN EN ISO 62

Send your message to this supplier

* From:
* To:

Ms. Tina
* Messages:

Enter between 20 to 4,000 characters.

Related Keywords

TECATRON PVX Bearing Grade PPS , Ensinger TECATRON PVX Polyphenylene Sulfide PPS , TECATRON PVX Stock Shapes Rods Plates Tubes