Heat Shrink Breakouts 5 Core , made of cross-linked polyolefin, is typically used to seal and protect low voltage cable terminals. Heat Shrink Breakouts 5 Core .
Features
1.Suitable for low voltage cables
2.Good sealing and adhesion capability
3.Highly ultraviolet and weather resistant
4.Min. shrink temperature: ≥110°C
5.Min. full recovery temperature: ≥130°C
6.Continuous operating temperature: -55°C~110°C
7.Standard color: black
Technical Performance
|
Properties |
Test Method |
Typical Data |
|
Tensile Strength |
ASTM D 2671 |
≥13 MPa |
|
Elongation at break |
ASTM D 2671 |
≥300% |
|
Tensile Strength after heat ageing |
ASTM D 2671/120°C, 168 hrs |
≥10 MPa |
|
Elongation after heat ageing |
150°C, 168 hrs |
≥250% |
|
Dielectric Strength |
IEC 243 |
≥15kV/mm |
|
Volume Resistivity |
IEC 93 |
≥1013Ω .cm |